Research electrolytic refining titanium tube technology issues medical titanium plate

After studying the literature , we did not use a non- aqueous medium and low temperature electrolysis of aqueous medium titanium tube method . Studied only the alkali metal and alkaline earth metal chlorides and fluorides Sunrui titanium plate consisting of salt melt and dissolved titanium compound. We know that a titanium 600 elements 900 ℃, gas (oxygen , nitrogen ) having a high reactivity , these impurities affect the mechanical properties of titanium , taking into account the impurities in the electrochemical process of Basking melt transfer medium titanium tube into the possibility of precipitation on the cathode , so we set ourselves a task - to establish the cell , in this cell to be able to ensure reliable external impurities in inert atmosphere and eliminate the possibility of contaminated electrolyte . In principle the use of certain widely used in modern technology , we are and how long after the test after a long quest to design and manufacture a large-scale experimental device , it can solve the problem in the electrolysis of pure titanium used in the relevant type electrolyte melt . In this device all the technical rules to determine the main electrolytic titanium tube test . Only in individual cases , in order to identify some of the issues , and only then move to a small laboratory tests on the device .

    To select an electrolytic refining process of titanium , titanium various titanium bar for sale compounds tested . Electrolysis of titanium trichloride, titanium tetrachloride, titanium fluoride , potassium titanium dioxide.

    Titanium trichloride having a high solubility in an alkali metal chloride into the electrolyte body . When the melt lift trichloride concentration - the timing of the electrolysis ; electrolysis precipitated on the titanium metal cathode , and deposited on the anode chloride , titanium ingot out of the electrolytic cell, and chlorine is here and after a combination of hydrogen supplied to the anode chloride .

    Because when not to use high-temperature electrolysis hydrogen , so start looking for other low-cost manufacturing methods chloride in the melt. Has been determined, if introduced into the graphite tube along the current, titanium flat bar while the steam through the graphite tube feeding TiCli , the current can disintegration of titanium tetrachloride reduction .